XC - Extra clean bright annealed or bright annealed and cold rolled Grease - Ultra-bright finish (for decorative applications) Soap - Soap is not removed from tempered wire to act as a lubricant. * Not all finishes are available in all alloys - Contact Ulbrich Sales for more information. Polished - Various grit finish for specific polish finished requirements. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. A light pass using highly polished rolls produces a glossy finish. # 2BA- Smooth finish produced by cold rolling and bright annealing. #CBA - Course bright annealed cold rolled matte finish and bright anneal #BA - Bright annealed cold rolled and bright annealed A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. # 2B - Smooth finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2D - Dull finish produced by cold rolling, annealing and descaling. It is used for applications where a smooth decorative finish is not required. It is available in strip, foil and ribbon. Refer to NACE (National Association of Corrosion Engineers) for recommendations. Additional Properties Corrosion Resistance of 316L For tempers 1 /2 hard or above consult Ulbrich Technical Services for more information. Type 316L can be cold rolled to achieve the temper properties required by specific customers and/ or manufacturing requirements. Yield Strength: (0.2% Offset) 75 KSI min (515 MPA min) Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength: (0.2% Offset) 55 KSI min (380 MPA min) Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength: (0.2% Offset) 45 KSI min (310 MPA min) Ultimate Tensile Strength: 85 KSI min (585 MPA min)

Ultimate Tensile Strength: 70 KSI min (485 MPa min) Yield Strength (0.2% Offset): 25 KSI min (170 MPa min) Elongation: 40% min Hardness: Rb 95 max Propertiesof 316L Stainless Strip in Tempered Conditions Melting Range: 2500 - 2590 ☏ (1371 - 1421 ☌) FormsĬoil - Strip, Foil, Ribbon Wire - Profile, Round, Flat, Square Mechanical Properties at Room Temperature Properties of 316L Stainless Strip in the Annealed Condition Magnetic Permeability: H = 200 Oersteds: Annealed < 1.02 max Mean Coefficient of Thermal Expansion: in/inl☏ (µm/m Thermal Conductivity: BTU/hr/ft2/ft/☏ (W/m What are the Physical Properties of 316L Stainless Steel?Įlectrical Resistivity: microhm-in (microhm-cm): What is the chemical composition of 316L Stainless Steel Strip? Element Type 316L is a low carbon austenitic chromium-nickel stainless steel with corrosion resistance similar to type 316 but with resistance to intergranular corrosion following welding. 316L Stainless Steel Strip, Coil, Foil, Wire Specification Codes: AMS 5507, ASTM A666 316L Stainless Steel Strip Applications

316l stainless steel composition